Polypropylene Sheet
Copolymer Polypropylene sheet is a versatile polymer used in a variety applications requiring chemical, corrosion, and impact resistance with a high strength to weight ratio. Polypropylene will not absorb moisture, is easy to form and meets FDA and USDA guidelines. This versatile combination of physical properties make polypropylene a common solution for many industrial applications.
Polypropylene has high dimensional stability and is easily machined, formed, or welded without losing its acid and abrasion resistance.
Copolymer Polypropylene sheet is a versatile polymer used in a variety applications requiring chemical, corrosion, and impact resistance with a high strength to weight ratio. Polypropylene will not absorb moisture, is easy to form and meets FDA and USDA guidelines. This versatile combination of physical properties make polypropylene a common solution for many industrial applications.
Polypropylene has high dimensional stability and is easily machined, formed, or welded without losing its acid and abrasion resistance.
Copolymer Polypropylene sheet is a versatile polymer used in a variety applications requiring chemical, corrosion, and impact resistance with a high strength to weight ratio. Polypropylene will not absorb moisture, is easy to form and meets FDA and USDA guidelines. This versatile combination of physical properties make polypropylene a common solution for many industrial applications.
Polypropylene has high dimensional stability and is easily machined, formed, or welded without losing its acid and abrasion resistance.
Common Applications for Polypropylene
Polypropylenes outstanding chemical resistance, ease of fabrication, welding and machining supports industrial applications including:
Structural Tanks and Linings
Plating Barrels
Ducts and Fume Hoods
Semiconductor Processing Equipment
Orthotic and Prosthetic Devices
Pump and Valve Components
Fire Truck Tanks
Laboratory Surfaces and Cabinets
Polypropylene Technical Data
| Property | Average Value (Metric) |
Average Value (Imperial) |
|---|---|---|
| Physical | ||
| Specific Gravity | 0.91 g/cc | 0.91 |
| Water Absorption at Saturation | <= 0.010% | <= 0.010% |
| Mechanical | ||
| Hardness, Shore D | 78 | 78 |
| Tensile Strength | 33.1 MPa | 4,800 psi |
| Elongation at Break | 25% | 25% |
| Tensile Modulus @ Temperature 22.8°C (73.0°F) | 2.07 GPa | 300 ksi |
| Flexural Strength | 41.4 MPa | 6,000 psi |
| Flexural Modulus | 1.72 GPa | 250 ksi |
| Compressive Strength | 48.3 MPa | 7,000 ps |
| Compressive Modulus | 1.31 GPa | 190 ks |
| Izod Impact, Notched | 0.641 J/cm | 1.20 ft-lb/in |
| Thermal | ||
| Melting Point | 162 °C | 324 °F |
| Maximum Service Temperature, Air | 82.2 °C | 180 °F |
| Deflection Temperature at 0.46 MPa (66 psi) | 104 °C | 220 °F |
| Deflection Temperature at 1.8 MPa (264 psi) | 82.2 °C | 180 °F |
| Flammability, UL94 | HB | HB |